Der Einfluss von Defekten auf das Schaltverhalten ferroelektrisch modulierter Substanzen
The influence of defects on the switching behaviour of ferroelectric modulated substances
von Karsten Behrendt
Datum der mündl. Prüfung:2015-07-21
Erschienen:2016-04-26
Betreuer:Prof. Dr. Götz Eckold
Gutachter:Prof. Dr. Götz Eckold
Gutachter:Prof. Dr. Dietmar Stalke
Gutachter:Prof. Dr. Ricardo Mata
Gutachter:Prof. Dr. Philipp Vana
Gutachter:Dr. Thomas Zeuch
Gutachter:Prof. Dr. Franc Meyer
Dateien
Name:Dissertation Behrendt.pdf
Size:4.09Mb
Format:PDF
Zusammenfassung
Englisch
The influence of defects on the phase transition behavior of A2BX4-compounds was studied by diffraction methods, impedance spectroscopy and atomic force microscopy. It was found that chemical point defects have a strong effect on the transition kinetics, whereas the thermodynamic stability of different modulated phases is only slightly affected by such doping with alkali ions. The lock-in-transition from incommensurate to commensurate modulated is slowed down by several orders of magnitude. The transition time hereby ranges from minutes to months, depending on impurity concentration. Due to this, metastable incommensurate phases can be obtained at room temperature. These undercooled phases exhibit remarkable structural and dielectric properties, such as polar nanodomains. The metastable phases undergo additional phase transitions into newly discovered commensurate phases. A unique property of those phases is a memory effect, which allows the incommensurate phase to be re-formed upon subsequent heating. A detailed microscopic model is discussed, which describes all aspects of the observed behavior. This model is based on the formation of a defect density wave and considers its interaction with discommensurations in the incommensurate phase. The thermodynamic properties of all observed phases can be deduced from this model.
Keywords: ferroelectric; incommensurate; defects; phase transition; permittivity; kinetics; atomic force microscopy; impedance spectroscopy; diffraction; metastable phases