dc.contributor.advisor Lieb, Klaus-Peter Prof. Dr. de
dc.contributor.author Müller, Georg Alexander de
dc.date.accessioned 2004-02-17T15:32:06Z de
dc.date.accessioned 2013-01-18T13:41:09Z de
dc.date.available 2013-01-30T23:51:12Z de
dc.date.issued 2004-02-17 de
dc.identifier.uri http://hdl.handle.net/11858/00-1735-0000-0006-B4EE-3 de
dc.description.abstract Magnetische "in-plane" Anisotropie ferromagnetischer dünner Filme ist von zentralem Interesse für die Entwicklung magnetischer Speichermedien. Dabei haben in den letzten Jahren unterschiedliche Methoden zur Präparation solcher anisotropen Filme und zur Erzeugung von magnetischen Strukturen an Bedeutung gewonnen.Im Rahmen dieser Arbeit wurde die Induktion der uniaxialen magnetischen in-plane Anisotropie dünner Eisenfilme durch Ionenbestrahlung untersucht. Die Filme wurden mittels Elektronenstrahlverdampfer oder gepulster Laserdeposition mit einer Dicke von ca. 75 nm erzeugt. Als Substrate wurden dabei Si(100), MgO(100) oder SiO2 benutzt. Es wurde der Einfluß von externer mechanischer Spannung, des externen Magnetfelds und der Filmmagnetisierung während der Ionenbestrahlung auf die Ausrichtung der magnetischen Anisotropie untersucht. Durch Variation der Projektilmasse (Xenon, Krypton, Eisen und Neon) und unter Beibehaltung der Ionenreichweite, wurde die Charakteristik der Ionen-Festkörper Wechselwirkung und damit die strukturelle Modifikation der Elektronenstrahlverdampften Filme variiert. Die resultierende magnetische Anisotropie wurde als Funktion der Ionendosis analysiert und mit den Veränderungen der mikroskopischen Spannungen und der Defektstruktur verglichen. Basierend auf diesen Ergebnissen wurde ein Mechanismus für die Entstehung der induzierten Anisotropie vorgeschlagen.Die experimentelle Analyse wurde mit einer Vielzahl von Techniken ausgeführt: Die magnetische Anisotropie wurde durch die Messung des magneto-optischen Kerr Effekts an einer im Rahmen dieser Arbeit aufgebauten Apparatur durchgeführt. Die Magnetische Orientierungs Mößbauer Spektroskopie lieferte zusätzliche Ergebnisse bezüglich der leichten Richtung des Films. Die Analyse der Probenstruktur erfolgte durch Röntgendiffraktion, Röntgenabsorption, Rutherford-Rückstreu-Spektroskopie und Sekundärionen-Massenspektroskopie. de
dc.format.mimetype application/pdf de
dc.language.iso eng de
dc.rights.uri http://webdoc.sub.gwdg.de/diss/copyrdiss.htm de
dc.title Ion-beam induced changes of magnetic and structural properties in thin Fe films de
dc.type doctoralThesis de
dc.title.translated Ionenstrahl induzierte Modifikation magnetischer und struktureller Eigenschaften dünner Eisenfilme de
dc.contributor.referee Münzenberg, Markus Prof. Dr. de
dc.date.examination 2004-01-20 de
dc.description.abstracteng Magnetic in-plane anisotropy of ferromagnetic thin films is of great interest for the development of magnetic data storage devices. In recent years, several methods for the preparation of such anisotropic films have been found and the ways of producing a magnetic nanostructure have been explored.In this thesis the uniaxial magnetic anisotropy of thin iron films, induced by ion implantation, was investigated. The 75 nm films were prepared via electron-beam evaporation or pulsed laser deposition, using Si(100), MgO(100) or SiO2 as the substrate. The influence of external mechanical stress, an external magnetic field, and the pre-magnetization of the film on the alignment of the anisotropy was studied. Additionally, the characteristics of the ion-solid interaction were modified by choosing projectiles with different mass (xenon, krypton, iron and neon) and keeping their penetration depth constant. The resulting magnetic anisotropy was analyzed as a function of the ion dose and correlated with the changes in the microscopic stress and ion induced defects of the film. On the basis of all the results, a model for the mechanism of ion induced magnetic anisotropy was proposed.The experimental analyses were performed by means of numerous techniques: the magnetic anisotropy was measured with the magneto-optical Kerr effect. The corresponding apparatus was set up in the course of this thesis. Additionally, magnetic orientation Mössbauer spectroscopy was carried out to obtain information about the easy axis of the film. The film structure was characterized by X-ray diffraction, X-ray absorption, Rutherford backscattering spectroscopy and secondary on-mass spectroscopy. de
dc.subject.topic Mathematics and Computer Science de
dc.subject.ger Ionenbestrahlung de
dc.subject.ger induzierte magnetische Anisotropie de
dc.subject.ger polykristalline dünne Eisenfilme de
dc.subject.ger Defektstruktur de
dc.subject.ger Elektronenstrahl Deposition de
dc.subject.ger PLD de
dc.subject.ger MOKE de
dc.subject.ger MOMS de
dc.subject.ger Spannungsanalyse de
dc.subject.ger RBS de
dc.subject.ger 530 Physik de
dc.subject.eng ion irradiation de
dc.subject.eng induced magnetic anisotropy de
dc.subject.eng polycrystalline thin Fe films de
dc.subject.eng defect structure de
dc.subject.eng electron-beam deposition de
dc.subject.eng PLD de
dc.subject.eng MOKE de
dc.subject.eng magnetic orientation Mössbauer spectroscopy de
dc.subject.eng stress analysis de
dc.subject.eng RBS de
dc.subject.bk 33.05 de
dc.subject.bk 33.68 de
dc.subject.bk 33.75 de
dc.identifier.urn urn:nbn:de:gbv:7-webdoc-297-0 de
dc.identifier.purl webdoc-297 de
dc.affiliation.institute Fakultät für Physik de
dc.subject.gokfull RVT 500: Bestrahlungseffekte in Metallen {Physik} de
dc.subject.gokfull RVC 860: Elektrische und magnetische Eigenschaften {Physik: Kristalline Festkörper} de
dc.identifier.ppn 386031819 de

Files in this item

This item appears in the following Collection(s)

Show simple item record